Preparation, characterization and microwave absorbing properties of carbon coated carbonyl iron nanostructure
محل انتشار: دومین کنفرانس بین المللی پژوهش در علوم و مهندسی
سال انتشار: 1395
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 470
فایل این مقاله در 13 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
ICRSIE02_227
تاریخ نمایه سازی: 11 مرداد 1396
چکیده مقاله:
In this study, the carbonyl iron was coated with carbon via hydrothermal reaction and the microwave absorption properties of the carbon coated carbonyl iron nanostructure (CI/C) was investigated in the range of 8.2-12.4GHz. The structure, characterization and magnetic performances of the prepared nanostructures were characterized by X-ray diffraction (XRD), transmission electron microscope (TEM) and vibrating sample magnetometer (VSM).The microwave properties including complex permittivity (εr), the permeability (μr), dielectric loss, magnetic loss, reflection loss, and attenuation constant were investigated using a vector network analyzer. For CI particles the optimal reflection loss for 4.4 mm thickness was -16.86 dB at the matching frequency of 12.3 GHz. The bandwidth with RL more than -10 dB can be reached in the frequency range of 10.8–12.4 GHz and there was no RL values below -20 dB. While for The CI/C nanostructure, the bandwidth of below-10 dB (90% power absorption) and -20dB (99% power absorption) can be obtained in the frequency range of 9.8–12.4 GHz and 11.0-11.8GHz respectively, As well as, the optimal RL was -46.69 dB at the matching frequency of 11.5GHz, when the matching thickness is 1.3 mm. The results indicate that the existence layer of C coated on CI, enhances the electromagnetic absorbing properties.
کلیدواژه ها:
Carbon coated carbonyl iron nanostructure ، Microwave absorption properties ، Hydrothermal reaction ، Reflection loss
نویسندگان
Hakimeh Pourabdolahi
Faculty of Chemistry and Chemical Engineering, Malek Ashtar University of Technology, P.O. Box ۱۵۸۷۵-۱۷۷۴, Tehran, Iran,
Ali Reza Zarei
Faculty of Chemistry and Chemical Engineering, Malek Ashtar University of Technology, P.O. Box ۱۵۸۷۵-۱۷۷۴, Tehran, Iran,
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :