Photocatalytic Activities of Anatase Nanoparticles Thin Film Coatings
محل انتشار: سومین کنگره بین المللی رنگ و پوشش
سال انتشار: 1388
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 1,749
فایل این مقاله در 8 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
ICCC03_057
تاریخ نمایه سازی: 6 اردیبهشت 1388
چکیده مقاله:
Anatase sol was synthesized by hydrolysis and condensation of titanium-n-butoxide in acidic aqueous condition. It was deposited on soda lime glass by spin coating method in room temperature. Characterization of sol and coatings were investigated. Results are demonstrated the mean particle size of the sol was in the range of 30-40 nm and did not change in the coating. In addition, the particle size distribution is uniform in the coating surface. Crystalline structure of deposited film is also investigated. Photocatalytic activities of films were studied by degradation of a colour indicator under different UV exposition time.
کلیدواژه ها:
نویسندگان
A Ershad-Langroudi
Colour, Resin & Surface Coatings (CRSC), Polymer Processing Department, Iran Polymer and Petrochemical Institute
D Zare-Hossein-abadi
Colour, Resin & Surface Coatings (CRSC), Polymer Processing Department, Iran Polymer and Petrochemical Institute
A Rahimi
Polymer Science Department, Iran Polymer and Petrochemical Institute
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :