A comparative study of the electrocatalytic oxidation of methanol on platinum particles electrodeposited into poly (1,5-diaminonaphthalene) film in acidic and alkaline media
محل انتشار: سومین همایش پیل سوختی ایران
سال انتشار: 1388
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 1,768
فایل این مقاله در 13 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
PEEL03_023
تاریخ نمایه سازی: 16 مرداد 1388
چکیده مقاله:
A new catalyst was prepared in which platinum particles were distributed into a poly (1,5-diaminonaphthalene) film onto glassy carbon electrode. Catalytic activity and stability of this modified electrode toward to oxidation of methanol were studied using cyclic voltammetry. For comparative purposes, sodium hydroxide and sulfuric acid solutions were used as testing solutions. This modified electrode shows significant different behavior in acidic and alkaline solutions. Enhanced electrocatalytic activity toward the oxidation of methanol was noticed when NaOH (1.0 M) solution was used as supporting electrolyte. A high catalytic current density for methanol oxidation (0.208 Acm−2) was found for the 1.0 M NaOH solutions in comparison to 0.5 M H2SO4 solutions (0.041 Acm−2).
کلیدواژه ها:
نویسندگان
Jahan Bakhsh Raoof
Department of Analytical Chemistry, Faculty of Chemistry, Mazandaran University, Babolsar, Iran Corresponding author
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :