Investigation on the Corrosion of Coated Steel Plates with Impact Defect using Divided Steel Plates
محل انتشار: ژورنال مهندسی عمران، دوره: 4، شماره: 1
سال انتشار: 1397
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 376
فایل این مقاله در 9 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_CEJ-4-1_005
تاریخ نمایه سازی: 6 آذر 1397
چکیده مقاله:
A method utilizing divided steel plates was used to investigate the corrosion of coated steel plates with impact defect while continuously submerged in 3% NaCl solution. The polarization behavior of circular divided steel plates was first compared to that of undivided ones. Half-cell potential and polarization resistance results show similar trend in divided and undivided form especially at the later stages of exposure. The method of using circular divided steel plates was then used to monitor the macrocell as well as microcell corrosion in coated steel plates induced with defect. The test results show that the defect causes macrocell corrosion to occur between the defect and sound portions. The impact defect also caused the reduction in the polarization resistance and consequently higher microcell corrosion at the neighbouring sound coated portions.
کلیدواژه ها:
نویسندگان
Marish S Madlangbayan
Associate Professor, University of the Philippines Los Baños, Laguna ۴۰۳۱, Philippines
Nobuaki Otsuki
Professor Emeritus, Tokyo Institute of Technology, Tokyo, Japan
Takahiro Nishida
Associate Professor, Kyoto University, Kyoto, Japan
Tsuyoshi Saito
Associate Professory,Niigata University, Niigata, Japan