Experimental Investigation of a Solid Oxide Fuel Cell Stack using Direct Reforming Natural Gas
سال انتشار: 1396
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 543
فایل این مقاله در 6 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_IJHFC-4-4_005
تاریخ نمایه سازی: 17 تیر 1398
چکیده مقاله:
In this study, a solid oxide fuel cell (SOFC) stack has been successfully fabricated and tested by using direct natural gas. The main objective of this research was to achieve optimal long-term performance of the SOFC stack without carbon deposition by using low-cost natural gas as a fuel. The stack configuration was improved by a new interconnect design and made of cost-effective raw materials. In this respect, the stack showed maximum power of 31 W while 33 A current was applied at a flow rate of 1000 ccm for H2 (as fuel) and oxygen. Then, humidified natural gas was employed as an internal reforming technique, which showed degradation of 1.4% after 24 h. Maximum obtained power was 32 W under 33 A current at a flow rate of 1000 ccm. After 48 h of operation, 34 W of power was achieved at the current of 38 A. Therefore, the power was increased from 32 to 34 W after 48 h of operation in upper current. Finally, a suitable SOFC stack made of cost effective materials and using direct natural gas under appropriate conditions was fabricated and developed in this research.
کلیدواژه ها:
نویسندگان
Morteza Torabi
Renewable Energy Department, Niroo Research Institute (NRI), Tehran, Iran
Mohammad Golmohammad
Renewable Energy Department, Niroo Research Institute (NRI), Tehran, Iran
Hamid Abdoli
Renewable Energy Department, Niroo Research Institute (NRI), Tehran, Iran
Hamed Mohebi
Renewable Energy Department, Niroo Research Institute (NRI), Tehran, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :