Preparation and characterization of Sr-Ti-hardystonite (Sr-Ti-HT) nanocomposite for bone repair application

محل انتشار: مجله علوم نانو، دوره: 2، شماره: 3
سال انتشار: 1394
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 430

فایل این مقاله در 8 صفحه با فرمت PDF قابل دریافت می باشد

استخراج به نرم افزارهای پژوهشی:

لینک ثابت به این مقاله:
https://civilica.com/doc/893498

شناسه ملی سند علمی:

JR_NAMJ-2-3_005

تاریخ نمایه سازی: 18 تیر 1398

چکیده مقاله:

Objective(s): Hardystonite (HT) is Zn-modified silicate bioceramics with promising results for bone tissue regeneration. However, HT possesses no obvious apatite formation. Thus, in this study we incorporated Sr and Ti into HT to prepare Sr-Ti-hardystonite (Sr-Ti-HT) nanocomposite and evaluated its in vitro bioactivity with the purpose of developing a more bioactive bone substitute material. Materials and methods:The HT and Sr-Ti-HT were prepared by mechanical milling and subsequent heat treatment. Calcium oxide (CaO), zinc oxide (ZnO) and silicon dioxide (SiO2) (all from Merck) were mixed with molar ratio of 2:1:2. The mixture of powders mixture was then milled in a planetary ball mill for 20 h. In the milling run, the ball-to-powder weight ratio was 10:1 and the rotational speed was 200 rpm. After synthesis of HT, 3% nanotitanium dioxide (TiO2, Degussa) and 3% strontium carbonate (SrCO3, Merck) were added to HT and then the mixture was ball milled and calcined at 1150°C for 6 h. Simultaneous thermal analysis (STA), X-ray diffraction (XRD), Transmission electron microscopy (TEM) and Fourier transform infra-red spectroscopy (FT-IR) performed to characterize the powders. Results:XRD and FT-IR confirmed the crystal phase and silicate structure of HT and TEM images demonstrated the nanostructure of powders. Further, Sr-Ti-HT induced apatite formation and showed a higher human mesenchymal stem cell (hMSCs) adhesion and proliferation compared to HT. Conclusion:Our study revealed that Sr-Ti-HT with a nanostructured crystal structure of 50 nm, can be prepared by mechanical activation to use as biomaterials for orthopedic applications.

کلیدواژه ها:

Apatite formation ، Hardystonite ، Mechanical activation ، Mesenchymal stem cells ، Nanocomposite

نویسندگان

Hossein Mohammadi

Department of Biomaterials, Science and Research Branch, Islamic Azad University, Yazd, Iran

Masoud Hafezi

Biomaterials Group, Nanotechnology and Advanced Materials Department, Materials and Energy Research Center, Alborz, Iran | Pardis Pajoohesh Fanavaran Yazd, BT center, Yazd Science and Technology Park, Yazd, Iran

Saeed Hesaraki

Biomaterials Group, Nanotechnology and Advanced Materials Department, Materials and Energy Research Center, Alborz, Iran

Mohammad Majid Sepantafar

Department of Stem Cell and Developmental Biology at Cell Science Research Center, Royan Institute for Stem Cell Biology and Technology, ACECR, Tehran, Iran

مراجع و منابع این مقاله:

لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :
  • De Aza PN, Fernández-Pradas JM, Serra P. In vitro bioactivity ...
  • El-Ghannam A, Ducheyne P, Shapiro IM. Porous bioactive glass and ...
  • Xue W, Liu X, Zheng X, Ding C. In vivo ...
  • Wu C. Methods of improving mechanical and biomedical properties of ...
  • Mohammadi H, Hafezi M, Nezafati N, Heasarki S, Nadernezhad A, ...
  • Yamaguchi M, Ehara Y. Zinc decrease and bone metabolism in ...
  • Yamaguchi M, Inamoto K, Suketa Y. Effect of essential trace ...
  • Yamaguchi M, Oishi H, Suketa Y. Zinc stimulation of bone ...
  • Capuccini C, Torricelli P, Sima F, Boanini E, Ristoscu C, ...
  • Fredholm YC, Karpukhina N, Law RV, Hill RG. Strontium containing ...
  • Harle J, Kim HW, Mordan N, Knowles JC, Salih V. ...
  • Vrouwenvelder WC, Groot CG, de Groot K. Better histology and ...
  • Wu C, Chang J, Zhai W. A novel hardystonite bioceramic: ...
  • Wu C, Ramaswamy Y, Chang J, Woods J, Chen Y, ...
  • Zreiqat H, Ramaswamy Y, Wu C, Paschalidis A, Lu Z, ...
  • Zhang M, Lin K, Chang J. Preparation and characterization of ...
  • Wu C, Chang J, Xiao Y. Advanced bioactive inorganic materials ...
  • Kokubo T, Takadama H. How useful is SBF in predicting ...
  • Wu C, Ramaswamy Y, Soeparto A, Zreiqat H. Incorporation of ...
  • Instrumentation AftAoM. Biological Evaluation of Medical Devices: Tests for Cytotoxicity, ...
  • Ciapetti G, Cenni E, Pratelli L, Pizzoferrato A. In vitro ...
  • Goudouri O, Theodosoglou E, Kontonasaki E, Will J, Chrissafis K, ...
  • Halliyal A, Hang KW, Haun MJ. Partially crystallizable glass compositions. ...
  • Tavangarian F, Emadi R. Mechanism of nanostructure bredigite formation by ...
  • Misevicius M, Scit O, Grigoraviciute-Puroniene I, Degutis G, Bogdanoviciene I, ...
  • Manso M, Langlet M, Martı́nez-Duart JM. Testing sol–gel CaTiO3 coatings ...
  • Agathopoulos S, Tulyaganov DU, Ventura JMG, Kannan S, Saranti A, ...
  • Zhang W, Shen Y, Pan H, Lin K, Liu X, ...
  • Williamson GK, Hall WH. X-ray line broadening from filed aluminium ...
  • Schrader B. Infrared and Raman spectroscopy: methods and applications: John ...
  • Kaushik A, Kumar J, Tiwari M, Khan R, Malhotra B, ...
  • Langlet M, Coutier C, Fick J, Audier M, Meffre W, ...
  • Iimori Y, Kameshima Y, Okada K, Hayashi S. Comparative study ...
  • Wu C, Chang J, Ni S, Wang J. In vitro ...
  • Mishra VK, Srivastava SK, Asthana BP, Kumar D. Structural and ...
  • Ardit M, Cruciani G, Dondi M. The crystal structure of ...
  • Li ZY, Lam WM, Yang C, Xu B, Ni GX, ...
  • Xiong K, Shi H, Liu J, Shen Z, Li H, ...
  • Arvanitidis I, Sichen D, Seetharaman S, Sohn HY. The intrinsic ...
  • Maitra S, Chakrabarty N, Pramanik J. Decomposition kinetics of alkaline ...
  • Hench LL. Biomaterials: a forecast for the future. Biomaterials. 1998; ...
  • Wu C, Chang J. A review of bioactive silicate ceramics. ...
  • Li P, Ohtsuki C, Kokubo T, Nakanishi K, Soga N, ...
  • Wu C, Ramaswamy Y, Kwik D, Zreiqat H. The effect ...
  • Oreffo RC, Cooper C, Mason C, Clements M. Mesenchymal stem ...
  • Mygind T, Stiehler M, Baatrup A, Li H, Zou X, ...
  • Marie PJ, Felsenberg D, Brandi ML. How strontium ranelate, via ...
  • Yamaguchi M. Role of nutritional zinc in the prevention of ...
    • نمایش کامل مراجع