Improving the Tribological Behavior of Commercially Pure Titanium Using TIG Surface Alloying
محل انتشار: مجله مواد دوستدار محیط، دوره: 1، شماره: 1
سال انتشار: 1396
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 408
فایل این مقاله در 6 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_JEFM-1-1_005
تاریخ نمایه سازی: 25 تیر 1398
چکیده مقاله:
Titanium alloys are widely applied to marine, biomaterials, chemical, petrochemical and automotive industries because of their unique property such as excellent creep resistance, corrosion resistance and relative higher specific strength ratio. However, they suffer from poor tribological properties such as low surface hardness and absolute values of tensile and shear strength which result in low wear resistance. On the other hand when Ti alloys are worn, they produce a dark-colored dust which is not environmental friendly. This project is aimed at producing hard and wear resistant particles in a matrix of Commercially Pure Titanium (CP-Ti) substrate by TIG (Tungsten Inert Gas) surface alloying. Different mixtures of Molybdenum and Titanium Carbide powders were applied to the surface in order to improve the hardness of surface layers. The microstructure of TIG alloyed layers were analyzed by OM, SEM and E-DAX. It was found that the hardness of the treated layers was more than three times higher than that of the CP-Ti substrate. Moreover, the wear resistance of this coatings were between 60 to150 times better than the base material.
کلیدواژه ها:
نویسندگان
A. Vahedi Nemani
Farayand Control Consulting Engineers Company, Tehran, Iran.
M. Ghaffari
Farayand Control Consulting Engineers Company, Tehran, Iran.
N. Rasekh Saleh
Islamic Azad University, East Tehran Branch (IAUET), Engineering Faculty.
H. Tazikeh
Mining and Metallurgical Department, Amirkabir University of Technology, Tehran, Iran.
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :